Thermal insulating paper LYTX-236B

Price: on request

Сeramic fiber paper is produced by high purity ceramic fiber and applied in the higher temperature heat insulation field. The advanced produce technology make the fiber in uniform distribution, also, the thickness of density are controlled strictly. In the production process, a few of binder is added with scientific selection and strictly control and the binder can be burning out in the application process. Luyang ceramic fiber paper with high density is a kind of fiber paper with high strength which is manufactured according to customer’s demand. It is with excellent heat insulation property and easy to construction. Also, the ceramic fiber paper is easy to future process (multilayer composite and cut). Luyang ceramic fiber isolation paper with excellent high temperature resistance and heat insulation performance and good melt infiltration resistance is very suitable for  using as off isolation casting gasket in building and glass industry.

 

Sizes

LYTX-236B

thickness, mm

length, mm

width, mm

 1

40 000

610

 2

30 000

610

 3

20 000

610

 4

20 000

610

 5

10 000

610

Type:
thermal insulating ceramic fiber paper.

Product characteristics:
• low heat storage
• low thermal conductivity
• excellent electrical insulation property
• excellent machining process property
• high strength, tear resistance
• low shot content
• high flexibility

Typical application:
• industrial heat insulation, sealing and corrosion protection materials.
• insulation and heat insulation materials used in instrument equipments and electric heating element.
• heat insulation materials in automotive and aerospace industry.
• expansion gap filler materials.
• isolation materials in building, metallurgy and glass industry.
• molten sealing gasket.
• fireproof materials.

Main technical characteristics

UOM

LYTX236B

Application temperature:
maximum
working



0
C

1260
1000

Density

kg/m3

200

Coefficient of thermal conductivity at a temperature:
600 0С
800 0С
1000 0С



W/m* K

0,14
0,20
0,22

Linear shrinkage after 24 hours of heating at a temperature 1000 0С

%

< -3

Heat capacity at a temperature 1000 0С

J

1130

An ultimate strength on a gap

MPa

> 0,3

Chemical composition:
Al2O3
SiO2


%

45-48
51-53

 

/** * */